By F. STOLBA.

Finely ground zircon is quickly rendered soluble if fused with a mixture of potassium borofluoride and potassium carbonate. The author takes two parts of the former to three of the latter, and prepares an intimate, finely divided mixture, which is kept ready for use.

Of this mixture four parts are taken to one of zircon, thoroughly mixed, and melted in a platinum crucible at a red heat. The mass fuses readily, froths at first and gives off bubbles of gas, and flows then quietly, forming a very fluid melt. If the zircon is finely ground, 15 minutes are sufficient for this operation. The loss of weight is 16 per cent., and is not notably increased on prolonged fusion. It corresponds approximately to the weight of the carbonic anhydride present in the potassium carbonate.

As pungent vapors are given off during fusion, the operation should be conducted under a draught hood. The activity of the mixture in attacking zircon appears from the following experiment: Two zircon crystals, each weighing ½ grm., were introduced into the melted mixture and subjected to prolonged heat. In a short time they decreased perceptibly in size; each of them broke up into two fragments, and within an hour they were entirely dissolved. The melted mass is poured upon a dry metal plate, and when congealed is thrown into water. It is at once intersected with a number of fissures, which facilitate pulverization. This process is the more necessary as the unbroken mass is very slowly attacked by water even on prolonged boiling. The powder is boiled in a large quantity of water so as to remove everything soluble. There is obtained a faintly alkaline solution and a sediment insoluble in water. From the filtrate alkalies throw down zirconium hydroxide, free from iron.

The portion insoluble in water is readily dissolved in hydrofluoric acid, and is converted into zircon potassium fluoride. The chief bulk of the zirconium is found in the aqueous solution in the state of double fluorides. The platinum crucible is not in the least attacked during melting. On the contrary, dirty platinum crucibles may be advantageously cleaned by melting in them a little of the above mentioned mixture.

If finely divided zircon is boiled for a long time with caustic lye, it is perceptibly attacked. It is very probable that in this manner zircon might be entirely dissolved under a pressure of 10 atmospheres.

Potassium borofluoride may be readily prepared from cryolite. Crucibles of nickel seem especially well adapted for the fusion of zircon in caustic alkalies. - Ber. Boehm. Gesell. Wissenschaft; Chem. News.